Irradiation of an aluminum alloy-clad, aluminum-uranium alloy-fueled plate /
Irradiation tests of an aluminum-alloy-clad aluminum -uranium alloy- fueled plate were discontinued due to cladding failure after a maximum burnup of 58%. Cause of the failure was local corrosion of the aluminum alloy. Swelling was observed which was attributed to the combination of high burnup and...